產(chǎn)品詳情
供應NSF51認證包裝材料PEI ULTEM 2100
ULTEM 2100玻纖10%填充NSF51認證PEI
ULTEM Resin 2100
PEI 基礎創(chuàng)新塑料（美國）2100-7301ULTEM 2100
10%玻璃纖維填充,標準流聚醚酰亞胺Polyetherimide(Tg 217 c)。符合ECO，阻燃UL94 V0 和5VA等級，通過NSF 51認證。包裝材料認證認可的顏色。
典型的屬性：
|
MECHANICAL |
Value |
Unit |
Standard |
|
Tensile Stress, yld, Type I, 5 mm/min |
1120 |
kgf/cm2 |
ASTM D 638 |
|
Tensile Strain, yld, Type I, 5 mm/min |
7 |
% |
ASTM D 638 |
|
Tensile Strain, brk, Type I, 5 mm/min |
60 |
% |
ASTM D 638 |
|
Tensile Modulus, 5 mm/min |
36500 |
kgf/cm2 |
ASTM D 638 |
|
Flexural Stress, yld, 2.6 mm/min, 100 mm span |
1680 |
kgf/cm2 |
ASTM D 790 |
|
Flexural Modulus, 2.6 mm/min, 100 mm span |
35800 |
kgf/cm2 |
ASTM D 790 |
|
Hardness, Rockwell M |
109 |
- |
ASTM D 785 |
|
Taber Abrasion, CS-17, 1 kg |
10 |
mg/1000cy |
ASTM D 1044 |
|
IMPACT |
Value |
Unit |
Standard |
|
Izod Impact, unnotched, 23°C |
136 |
cm-kgf/cm |
ASTM D 4812 |
|
Izod Impact, notched, 23°C |
5 |
cm-kgf/cm |
ASTM D 256 |
|
Izod Impact, Reverse Notched, 3.2 mm |
136 |
cm-kgf/cm |
ASTM D 256 |
|
Gardner, 23°C |
373 |
cm-kgf |
ASTM D 3029 |
|
THERMAL |
Value |
Unit |
Standard |
|
Vicat Softening Temp, Rate B/50 |
218 |
°C |
ASTM D 1525 |
|
HDT, 0.45 MPa, 6.4 mm, unannealed |
210 |
°C |
ASTM D 648 |
|
HDT, 1.82 MPa, 6.4 mm, unannealed |
201 |
°C |
ASTM D 648 |
|
CTE, -20°C to 150°C, flow |
5.58E-05 |
1/°C |
ASTM E 831 |
|
CTE, -20°C to 150°C, xflow |
5.4E-05 |
1/°C |
ASTM E 831 |
|
Thermal Conductivity |
0.22 |
W/m-°C |
ASTM C 177 |
|
Relative Temp Index, Elec |
170 |
°C |
UL 746B |
|
Relative Temp Index, Mech w/impact |
170 |
°C |
UL 746B |
|
Relative Temp Index, Mech w/o impact |
170 |
°C |
UL 746B |
|
PHYSICAL |
Value |
Unit |
Standard |
|
Specific Gravity |
1.27 |
- |
ASTM D 792 |
|
Water Absorption, 24 hours |
0.25 |
% |
ASTM D 570 |
|
Water Absorption, equilibrium, 23C |
1.25 |
% |
ASTM D 570 |
|
Mold Shrinkage, flow, 3.2 mm (5) |
0.5 - 0.7 |
% |
SABIC Method |
|
Melt Flow Rate, 337°C/6.6 kgf |
9 |
g/10 min |
ASTM D 1238 |
|
ELECTRICAL |
Value |
Unit |
Standard |
|
Volume Resistivity |
1.E+17 |
Ohm-cm |
ASTM D 257 |
|
Dielectric Strength, in air, 1.6 mm |
32.7 |
kV/mm |
ASTM D 149 |
|
Dielectric Strength, in oil, 1.6 mm |
27.9 |
kV/mm |
ASTM D 149 |
|
Dielectric Strength, in oil, 3.2 mm |
19.6 |
kV/mm |
ASTM D 149 |
|
Relative Permittivity, 100 Hz |
3.15 |
- |
ASTM D 150 |
|
Relative Permittivity, 1 kHz |
3.15 |
- |
ASTM D 150 |
|
Dissipation Factor, 100 Hz |
0.0015 |
- |
ASTM D 150 |
|
Dissipation Factor, 1 kHz |
0.0012 |
- |
ASTM D 150 |
|
Dissipation Factor, 2450 MHz |
0.0025 |
- |
ASTM D 150 |
|
Arc Resistance, Tungsten {PLC} |
5 |
PLC Code |
ASTM D 495 |
|
Hot Wire Ignition {PLC) |
1 |
PLC Code |
UL 746A |
|
High Voltage Arc Track Rate {PLC} |
2 |
PLC Code |
UL 746A |
|
High Ampere Arc Ign, surface {PLC} |
3 |
PLC Code |
UL 746A |
|
Comparative Tracking Index (UL) {PLC} |
4 |
PLC Code |
UL 746A |
|
FLAME CHARACTERISTICS |
Value |
Unit |
Standard |
|
UL Recognized, 94V-2 Flame Class Rating (3) |
0.4 |
mm |
UL 94 |
|
UL Recognized, 94V-0 Flame Class Rating (3) |
0.75 |
mm |
UL 94 |
|
UL Recognized, 94-5VA Rating (3) |
3 |
mm |
UL 94 |
|
Oxygen Index (LOI) |
47 |
% |
ASTM D 2863 |
|
NBS Smoke Density, Flaming, Ds 4 min |
0.7 |
- |
ASTM E 662 |
聚醚酰亞胺PEI （Polyetherimide），PEI 是琥珀色透明固體，不添加任何添加劑PEI原料顆粒圖片就有固有的阻燃性和低煙度，氧指數(shù)為47%，燃燒等級為UL94-V-0級，密度為1.28~1.42g/cm3。PEI具有很強的高溫穩(wěn)定性，即使是非增強型的PEI，仍具有很好的韌性和強度。因此利用PEI優(yōu)越的熱穩(wěn)定性可用來制作高溫耐熱器件。具有優(yōu)良的機械性能、電絕緣性能、耐輻照性能、耐高低溫及耐磨性能，并可透過微波。
PEI(聚醚酰亞胺)具有優(yōu)良的機械性能、電絕緣性能、耐輻照性能、耐高低溫及耐磨性能，并可透過微波。PEI兼具優(yōu)良的高溫機械性能和耐磨性，故可用于制造輸水管轉向閥的閥件。由于具有很高的強度、柔韌性和耐熱性，PEI是優(yōu)良的涂層和成膜材料，能形成適用于電子工業(yè)的涂層和薄膜。 主要特點 連續(xù)工作溫度范圍大（-200--170度長期工作），玻璃化溫度與熱變性溫度接近、熔點高達330度 在低溫/高溫下仍保有高機械強度、高硬度、高抗蠕變性、良好韌性 杰出的抗析出性 ( 適合用在利用蒸氣消毒的殺菌室 )；不易滋生細菌，常用于食品加工業(yè) 高抗輻射性優(yōu)異、可透過紅外光和微波輻射；電器絕緣性好、良好的電鍍性能 較寬溫度（-200--170度）范圍保持穩(wěn)定的介電常數(shù)和損耗因數(shù) 不能通過SMT回流焊接測試 主要應用 電子行業(yè)：連接件、普通和微型繼電器外殼、電路板、線圈、軟性電路、反射鏡、高精度密光纖元件、高溫隔熱板 汽車行業(yè)：連接件、高功率車燈和指示燈、控制汽車艙室外部溫度的傳感器、控制空氣和燃料混合物溫度的傳感器，醫(yī) 療器材等。