產(chǎn)品詳情
BÖHLER FOX CEL Mo Stick electrode
Classifications unalloyed cellulosic
EN ISO 2560-A: AWS A5.5:
E 42 3 Mo C 2 5 E7010-A1
Characteristics and field of use
Higher-strength, cellulose coated Stick electrode for vertical down welding0n large pipelines.
Highly economical compared to vertical up welding. Particularly suitable for hot pass, filler and
cover pass welding0n higher-strength pipe steels. BÖHLER FOX CEL Mo is characterised by a
very intensive, fine-droplet depositing, as well as good toughness properties. Insensitive to weather
conditions, high resistance to the bation of shrinkage grooves. HIC and SSC resistance tested
according to NACE TM 02-84 or TM 01-77.
Base materials
S235JR, S275JR, S235J2G3, S275J2G3, S355J2G3, P235GH, P265GH, L210-L415NB, L290MB
– L415MB, P355T1, P235T2-P355T2, P235G1TH, P255G1TH root pass up to L555MB API Spec. 5
L: Grade A, B, X 42, X 46, X 52, X 56, X 60, root pass up to X 80
Typical analysis of all-weld bl (Wt-%)
C Si Mn Mo
0.1 0.14 0.4 0.5
Mechanical properties of all-weld bl
Heat
Treatment
Yield
strength
0.2%
Tensile
strength
Elongation
(L0=5d0)
Impact values
ISO-V
MPa MPa % 20°C ±0°C –20°C –30°C -40°C
untreated 480 550 23 100 95 85 50 42
Operating data
Polarity = + / = -
Minus Polarity for root pass0nly
Dimensions (mm) Amperage A
3.2 x 350 80-130
4.0 x 350 120-180
5.0 x 350 140-210
Approvals and certificates
TüV (11181.), CE
Classifications unalloyed cellulosic
EN ISO 2560-A: AWS A5.5:
E 42 3 Mo C 2 5 E7010-A1
Characteristics and field of use
Higher-strength, cellulose coated Stick electrode for vertical down welding0n large pipelines.
Highly economical compared to vertical up welding. Particularly suitable for hot pass, filler and
cover pass welding0n higher-strength pipe steels. BÖHLER FOX CEL Mo is characterised by a
very intensive, fine-droplet depositing, as well as good toughness properties. Insensitive to weather
conditions, high resistance to the bation of shrinkage grooves. HIC and SSC resistance tested
according to NACE TM 02-84 or TM 01-77.
Base materials
S235JR, S275JR, S235J2G3, S275J2G3, S355J2G3, P235GH, P265GH, L210-L415NB, L290MB
– L415MB, P355T1, P235T2-P355T2, P235G1TH, P255G1TH root pass up to L555MB API Spec. 5
L: Grade A, B, X 42, X 46, X 52, X 56, X 60, root pass up to X 80
Typical analysis of all-weld bl (Wt-%)
C Si Mn Mo
0.1 0.14 0.4 0.5
Mechanical properties of all-weld bl
Heat
Treatment
Yield
strength
0.2%
Tensile
strength
Elongation
(L0=5d0)
Impact values
ISO-V
MPa MPa % 20°C ±0°C –20°C –30°C -40°C
untreated 480 550 23 100 95 85 50 42
Operating data
Polarity = + / = -
Minus Polarity for root pass0nly
Dimensions (mm) Amperage A
3.2 x 350 80-130
4.0 x 350 120-180
5.0 x 350 140-210
Approvals and certificates
TüV (11181.), CE