牌號
|
ML15Al冷鐓冷擠壓用鋼
|
|
|
|
|
|
|
|
|
|
中國ISC
|
U40158
|
|
|
|
|
|
|
|
|
|
對應(yīng)標(biāo)準(zhǔn)
|
GB T 6478-2001
|
|
|
|
|
|
|
|
|
|
冷鐓和冷擠壓用鋼
|
|
|
|
|
|
|
|
|
|
Steels for cold heading and cold extruding
|
|
|
|
|
|
|
|
|
|
歸類
|
碳鋼
|
|
|
|
|
|
|
|
|
|
標(biāo)簽
|
鋁zhen靜鋼
|
|
|
|
|
|
|
|
|
|
ML15Al 化學(xué)元素成分含量(%)
|
|
|
|
|
|
|
|
|
|
|
成分
|
C
|
Si ®
|
Mn
|
P
|
S
|
Cr *
|
Ni *
|
Cu *
|
Al ?
|
|
最小值
|
0.13
|
-
|
0.3
|
-
|
-
|
-
|
-
|
-
|
0.02
|
|
最大值
|
0.18
|
0.1
|
0.6
|
0.035
|
0.035
|
0.2
|
0.2
|
0.2
|
-
|
|
①經(jīng)供需雙方協(xié)議，可供應(yīng)其他牌號的冷鐓鋼和冷擠壓用鋼
|
|
|
|
|
|
|
|
|
|
|
②鋼材的化學(xué)成分允許偏差應(yīng)符合GB/T 222-1984的相關(guān)規(guī)定。
|
|
|
|
|
|
|
|
|
|
|
?為鋼中的總鋁量
|
|
|
|
|
|
|
|
|
|
|
*為鋼中的殘余元素含量
|
|
|
|
|
|
|
|
|
|
|
®采用堿性電爐冶煉時(shí)，鋼中的硅含量不得大于0.17%
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
ML15Al 機(jī)械性能
|
|
|
|
|
|
|
|
|
|
|
條件
|
熱處理或狀態(tài)
|
抗拉強(qiáng)度
|
屈服點(diǎn)
|
斷后伸長率或延伸率
|
斷面收縮率
|
硬度
|
|
|
|
|
σb
|
σs
|
δ
|
ψ
|
HBW
|
|
|
|
|
Mpa
|
Mpa
|
%
|
%
|
|
|
|
|
|
鋼材
|
熱軋
|
≤530
|
|
|
≥50
|
|
|
|
|
|
鋼材
|
退火
|
≤470
|
|
|
*
|
|
|
|
|
|
≥64
|
|
|
|
|
試樣直徑d=25
|
熱處理
|
450~750
|
≥260
|
≥14
|
|
熱軋布氏硬度HBS
|
|
|
|
|
≤143
|
|
|
|
|
*鋼材直徑不大于12mm時(shí)，斷面收縮率可降低2%
|
|
|
|
|
|
|
|
|
|
|
※熱處理制度：
|
|
|
|
|
|
|
|
|
|
|
滲碳溫度880~980°C，直徑淬火溫度830~870°C，雙重淬火溫度 心部淬硬880~920°C 表面淬硬780~820°C，回火溫度150~200°C
|
|
|
|
|
|
|
|
|
|
|
以上溫度只是推薦值，實(shí)際選擇的溫度應(yīng)以使性能達(dá)到要求為準(zhǔn)。
|
|
|
|
|
|
|
|
|
|
|
滲碳溫度取決于鋼的化學(xué)成分和滲碳介質(zhì)。一般情況下，如鋼直接淬火，不要超過950°C。
|
|
|
|
|
|
|
|
|
|
|
淬火劑的種類取決于產(chǎn)品形狀、冷卻條件和爐子裝料的數(shù)量。
|
|
|
|
|
|
|
|
|
|
|
回火時(shí)間推薦最少1h。
|
|
|
|
|
|
|
|
|
|