產(chǎn)品詳情
日本日亞NH610S模具焊條 NH-610
日本日亞NH610S模具焊條 NH-610
|
特 性 |
高鉻成份,焊金具有高拉力,高韌性 HB-280. High chrome component, high strength, welding gold high toughness HB - 280. |
|
用 途 |
鑄鋼模硬面制做打底緩沖層,裂縫敏感度較高的特種鋼接合襯焊使用. Cast steel hardfaced making render buffer layer, crack sensitive use of special steel lining welding joints. |
|
規(guī) 格 |
2.6￠ 3.2￠ |
TM-2000模具硬化堆焊用
|
特 性 |
對(duì)沖壓模的金屬磨耗非常有效,焊金第一次為奧氏體組織,第二層為高硬度的馬氏體組織.火焰淬火鋼也可以直接堆焊. The bl stamping mould for abrasion is very effective for the first time, welding gold austenitic organization, the second is the high hardness martensite steel quenching. Flame may also directly hardfacing. |
|
用 途 |
直接堆焊各種鑄鐵材的模具. All sorts of cast iron material directly surfacing of mould. |
|
規(guī) 格 |
2.6￠ 3.2￠ 4.0￠ 5.0￠ |
LKE-7號(hào)鋼焊條(SUPER-7)
|
特 性 |
耐沖擊與金屬間磨耗,直接焊于熱處理后的Cr12MoV鋼上,可全位置焊接,硬度HRC52~57. Impact resistance and bl abrasion, directly welded to the Cr12MoV after heat treatment, but the POSTTTION on the steel welding, hardness HRC52-57 |
|
用 途 |
汽車大型模具硬面制做,冷沖模刀口焊接Auto giant mould making, cold die cutting hardfaced welding. |
|
規(guī) 格 |
2.6￠ 3.2￠ |
GNK-7A刃口焊條
|
特 性 |
熔敷金屬具有高硬度的馬氏體組織,耐磨耗耐沖擊性能優(yōu)良,硬度HRC55~58. Deposited bl of martensite with high hardness, good abrasion resistance, impact resistant perbance of hardness HRC55 ~ 58. |
|
用 途 |
切模,沖壓模具的刃口焊材,也可以在碳鋼上堆焊制成新工具. Cutting, welding blade of stamping mould, also can be made in the new tool steel #. |
|
規(guī) 格 |
2.6￠ 3.2￠ 4.0￠ |
CARBO 6W各種刃口堆焊使用
|
特 性 |
高鉻成份,耐磨耗耐龜裂性能優(yōu)良,焊后硬度較高,機(jī)械加工困難. High chrome component, abrasion resistance, resistance to crack excellent perbance after welding, machining difficulty high hardness. |
|
用 途 |
淬火硬化模具鋼刃口的修補(bǔ),適用于SKD11合金工具鋼,淬火后的模具鋼修補(bǔ). Quench hardened steel blade of repair, applicable to SKD11 alloy steel, alloy after quenching repair. |